Home Company Products Workshop News Industry dynamics KnowledgeTrade Area Case Culture Technical support Contact CHINESE
     
 
PRODUCT LIST
  Fence Series
·Road Fence
·Railway Fence
·Airport Fence
·Bridge Protection Fence
·Housing Estate Fence
·Plant Area Fence
·Prison Fence
·Workshop Fence
·Temporary Fence
·Court Fence
·Palisade
·Prairie Fence
·Invisible protective mesh
  Other Fence Series
·Peach Column Separation Fence
·Uptown Separation Fence
·Municipal Separation Fence
·Development Zone Separation Fence
·Airport Separation Fence
·Frame Separation Fence
·Highway Fence
·Railway Separation Fence
CONTACT US
Tel:86-318-5182058 7859868
Mobole:86-15931361333   13653182308
Fax:86-318-7859868
Con:MIss Liu
E-mail:sales@hbpzhlw.com
Url:www.hbpzhlw.com
Add:LiGeZhuang Development Zone, Anping County, Hebei P.R., China
You Site>>Hebei Pengze Hardware Products Co., Ltd.>>Knowledge
隔离栅材质低碳钢焊接的特点有哪些?
作者:  来源:  发表时间:2011-8-25 11:14:29  点击:25

由于低碳钢含碳量低,锰、硅含量也少,所以,通常情况下不会因焊接而产生严重硬化组织或淬火组织。低碳钢焊后的接头塑性和冲击韧度良好,焊接时,一般不需预热、控制层间温度和后热,焊后也不必采用热处理改善组织,整个焊接过程不必采取特殊的工艺措施,焊接性优良。 但在少数情况下,焊接时也会出现困难:

1)采用旧冶炼方法生产的转炉钢含氮量高,杂质含量多,从而冷脆性大,时效敏感性增加,焊接接头质量降低,焊接性变差。

2)沸腾钢脱氧不完全,含氧量较高,P等杂质分布不均,局部地区含量会超标,时效敏感性及冷脆敏感性大,热裂纹倾向也增大。

3)采用质量不符合要求的焊条,使焊缝金属中的碳、硫含量过高,会导致产生裂纹。如某厂采用酸性焊条焊接Q235-A钢时,因焊条药皮中锰铁的含碳量过高,会引起焊缝产生热裂纹。

4)某些焊接方法会降低低碳钢焊接接头的质量。如电渣焊,由于线能量大,会使焊接热影响区的粗晶区晶粒长得十分粗大,引起冲击韧度的严重下降,焊后必需进行细化晶粒的正火处理,以提高冲击韧度。 总之,低碳钢是属于焊接性最好、最容易焊接的钢种,所有焊接方法都能适用于低碳钢的焊接。

 